Effects of annealing treatment on the properties of MEH-PPV/titania hybrids prepared via in situ sol–gel reaction

Abstract

A uniform poly[2-methoxy-5-(2′-ethylhexyloxy)- p-phenylenevinylene] (MEH-PPV)/titania hybrid film was successfully prepared by an in situ sol–gel reaction of titanium isopropoxide (TIP) in the presence of MEH-PPV/2-chlorophenol solution. The annealing treatment increased the conversion of TIP to titania as determined from evidence of the formation of Ti–O–Ti bonds in the Fourier transform infrared (FTIR) spectrum. Scanning electronic microscope (SEM) photographs showed that the morphology and distribution of titania in the hybrid film were strongly related to the amount of water in the in situ sol–gel reaction. The thermal stability of MEH-PPV/titania hybrids was enhanced by the annealing treatment. Small angle X-ray scattering (SAXS) and X-ray diffraction (XRD) analyses indicated that annealing treatment promoted the ordered aggregation of the MEH-PPV chains and crystallization of titania to a certain extent. The blue shift in Ultraviolet–visible (UV–vis) absorption of pure MEH-PPV after annealing was ascribed to the small extent of decomposition and coil conformation which occurred at high temperature. A more-obvious blue shift for the hybrids was observed, which resulted from irregular aggregation and coil conformation of the MEH-PPV chains induced by heterogeneous point, TIP (titania). The red shift in the photoluminescent (PL) emission for pure MEH-PPV resulted from a certain extent of ordered aggregation after annealing. However, only a slight red shift in the PL emission peak for the hybrids was found due to the hindrance of ordered aggregation of MEH-PPV chains in the presence of TIP (titania).