Abstract
The preparation of mesocarbon microbeads (MCMB) had been carried out by heat-treating a medium coal tar pitch at 420degC for 2 hours in the presence of aluminum chloride(AlCl3). A larger number of MCMB with small diameter were obtained. The isolated MCMB were observed by scanning electron microscope. The average diameters of the MCMB were measured by laser particle size analyzer. The Pl(pyridine insoluble) yields were determined from the weight of the extracted residue. The effects of AlCl3 on preparation of MCMB had been studied. It was found that AlCl3 promotes the formation of MCMB in coal tar pitch. The sphere size and PI yield increase with increasing in the amount of AlCl3, the size distribution becomes wide gradually at the same time. The amount of AlCl3 from 3 to 5 wt% appears opfimurn to give small MCMB, diameter below 8 mum, with good spherical shape and smooth surface at PI yield over 40 wt%.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.