Effects of aging procedures on the topographic surface, structural stability, and mechanical strength of a ZrO2-based dental ceramic

Abstract

ObjectiveTo determine the effects of different aging methods on the degradation and flexural strength of yttria-stabilized tetragonal zirconia (Y-TZP) MethodsSixty disc-shaped specimens (∅, 12mm; thickness, 1.6mm) of zirconia (Vita InCeram 2000 YZ Cubes, VITA Zahnfabrik) were prepared (ISO 6872) and randomly divided into five groups, according to the aging procedures (n=10): (C) control; (M) mechanical cycling (15,000,000 cycles/3.8Hz/200N); (T) thermal cycling (6,000 cycles/5–55°C/30s); (TM) thermomechanical cycling (1,200,000 cycles/3.8Hz/200N with temperature range from 5°C to 55°C for 60s each); (AUT) 12h in autoclave at 134°C/2bars; and (STO) storage in distilled water (37°C/400 days). After the aging procedures, the monoclinic phase percentages were evaluated by X-ray diffraction (XRD), and topographic surface analysis was performed by 3D profilometry. The specimens were then subjected to biaxial flexure testing (1mm/min, load 100kgf, in water). The biaxial flexural strength data (MPa) were analyzed by 1-way ANOVA and Tukey's test (α=0.05). The data for monoclinic phase percentage and profilometry (Ra) were analyzed by Kruskal–Wallis and Dunn's tests. ResultsANOVA revealed that flexural strength was affected by the aging procedures (p=0.002). The M (781.6MPa) and TM (771.3MPa) groups presented lower values of flexural strength than did C (955MPa), AUT (955.8MPa), T (960.8MPa) and STO (910.4MPa). The monoclinic phase percentage was significantly higher only for STO (12.22%) and AUT (29.97%) when compared with that of the control group (Kruskal–Wallis test, p=0.004). In addition, the surface roughnesses were similar among the groups (p=0.165). SignificanceWater storage for 400 days and autoclave aging procedures induced higher phase transformation from tetragonal to monoclinic; however, they did not affect the flexural strength of Y-TZP ceramic, which decreased only after mechanical and thermomechanical cycling.