Formation of intermetallic compounds (IMCs) in solder joints is closely associated with the mechanical reliability of the system. Though internal voids formed in Ni/Sn solder joints are known to be related to the formation of Ni3Sn4 IMC, a detailed study on the mechanical reliability has not yet been reported. In this study, the mechanical reliability of Ni/Sn joints was investigated using two different soldering systems: Ni/Ag-Ag/Sn/Ni bilayers and Ni/Sn/Ag-Ag/Sn/Ni sandwich structures. The failure mode was found to be closely related to the formation and growth of an Ag3Sn phase. Filling of the voids with Ag3Sn IMC resulted in maximum shear strength, with a failure locus through Ni3Sn4 and Ag3Sn. However, formation of a large amount of Ag3Sn decreased the shear strength once again.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.