Abstract
The technology of bonded composite repair has displayed its effectiveness in increasing the residual fatigue life of cracked aeronautical structures. However, two major phenomena reduce the performance of this technique; the adhesive disbond by the fatigue load and the thermal residual stresses due to the adhesive curing. In this study, the effects of the adhesive disbond and the thermal residual stresses on the fatigue life of repaired cracked aluminum plate were analyzed experimentally and numerically. Fatigue tests were performed on cracked 2024-T3 aluminum alloy specimens repaired using carbon/epoxy patches that have artificial disbonds, to highlight the adhesive disbond effect. Fatigue tests were performed on repaired specimen bonded with elevated temperature cure and ambient temperature cure adhesives to evaluate the effect of the thermal residual stresses. To analyze the effects of the two phenomena, the finite element method was used to compute the stress intensity factor at the front of repaired cracks. The experimental results indicate that fatigue life is significantly reduced by the presence of an initial adhesive disbond and thermal residual stresses. The numerical results are consistent with the experimental observations, and reveal that the stress intensity factor increases with an increase in the disbond width. Moreover, it also increases in the presence of thermal residual stresses.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.