Abstract
High-purity alumina ceramics was prepared using high-purity α-Al2O3 powder as raw material, nitrates or oxides of magnesium, chromium and copper as additives by a wet ball milling with a later dry pressing forming and normal pressure sintering process. The influence of additives on the sintering temperature, microstructure and bending strength of the prepared alumina ceramics was studies. The results showed that the additive doped with nitrate can be dispersed uniformly in the body with molecule scale, and the oxides obtained by decomposing of nitrates have the higher reactivity. Thus, the nitrate additives have better capacity than oxide additives in reducing the sintering temperature and inhibiting the abnormal grain growth, and the alumina ceramics prepared by adding of nitrate additives have higher density and bending strength.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.