Abstract
AbstractWater or acid soaking surface treatments have been shown to increase the mechanical strength of soda‐lime silicate (SLS) glasses. This increase in strength has traditionally been attributed to effects related to residual stress or changes in fracture resistance. In this work, we report experimental data that cannot be explained based on the existing knowledge of glass surface mechanics. In dry environments, annealed and acid‐leached SLS surfaces have comparable crack initiation stress and fracture stress as measured by Hertzian indentation and biaxial bending tests, respectively. Yet, in the presence of humidity, acid‐leached surfaces have higher failure stress than the annealed surfaces. This apparent enhancement in the crack resistance of the acid‐leached surface of SLS glass in humid environments supports the hypothesis that acid‐leached surface chemistry can lower the transport kinetics of molecular water to critical flaws.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.