Abstract
Based on previous observations that a pressurized water treatment (PWT) prevented cracking of sol–gel microspheres, we investigated the effects of a PWT on microsphere crystallinity, density, and specific surface area (SSA). Results were used to determine how a PWT alters the properties of microspheres upon drying and heating. Microspheres with diameters near 100–200 µm were prepared with and without a PWT and measured using x-ray diffraction (XRD), transmission electron microscopy (TEM), nitrogen adsorption (BET), and pycnometry. Properties of air-dried microspheres processed with and without a PWT are compared. In addition, the properties of microspheres processed using a PWT are reported after heating to 150, 450, 750, 1050, and 1350 °C. XRD measurements indicate that the PWT step improves the crystallinity of air-dried microspheres. XRD data were also used to calculate crystallite size, which increases with higher heat-treatment temperatures. TEM images support crystallite size calculations from XRD data and provide an indication of the range of crystallite sizes, particularly for samples processed at higher temperatures where crystallite sizes are too large for estimation using the Scherrer formula. Density and SSA measurements performed as a function of heat-treatment temperature indicate that a PWT increases the density of air-dried microspheres, creates a pore network, and that significant densification occurs between 450 and 750 °C. These results may be used to inform decisions on internal gelation flowsheet parameters to optimize the microsphere formation and gelation step, prevent microsphere cracking, and produce microspheres suitable for subsequent coating operations or pressing into pellets.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.