Abstract
This work aims to reveal the effects of 3D roughness parameters of sandblasted surfaces on bond strength between thermal spray coatings and substrates. The investigation was carried out on the surface of AISI 4140, which were pretreated with automatic-sandblasting system. 3D topography and roughness parameters were analyzed by a 3D optical profiler. The bond strength of WC-12Co coatings was measured using a pull-off test method. Scanning electron microscope revealed that the morphology of the surface after sandblasting was rough. Furthermore, the surface topography was characterized by several irregular peaks and pits with different directions and no fixed orientation randomly distributed on sandblasted surface. The average values for surface roughness Sa = 4.84 ± 0.34 μm and bond strength = 32.8 ± 2.8 MPa were obtained. In terms of 3D roughness parameters, Sa, Sdr, Sdq and Sq were found to have more significant impact on affecting the bond strength, showing a nonlinear regression relationship. Furthermore, bond strength was positively correlated with Sa, Sdr and Sdq, while inversely proportional to Sq. This confirmed that a greater surface roughness of a sandblasted surface was not more conducive to the improvement of bond strength. The influence mechanism of each parameter was discussed, which was consistent with the regression mathematical model.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.