Abstract
Nano size of ceramic filler (nanofiller) are tend to possess difficulties to be covered by resin matrix due to large surface area to volume ratio. Addition of aceton known as the diluent agent by introducing more content of filler as well as helping distribution of the filler in the resin matrix in application of dental composite restoration. In this study, a total 24 specimens of dental composite prototype; nanofiller-TMPS and nanofiller-MPTS were prepared using a customized acrylic mold and they were divided into two groups based on filler/resin ratio (n=6 each group). In the process of dental composite making, acetone were added into resin; 1 ml (filler/resin, 50/50) and 5 ml (filler/resin, 80/20) untill specific consistency obtained. The specimens were stored in distilled water for 24 hours at 37°C then subjected to hardness test using Vickers hardness tester machine, LECO – Japan M– 400–H1 with the load of 200 grams for 15 seconds (ADA Specification No. 27). Data were statistically analyzed using t independent test (α=0.05). The result revealed that dental composite prototype contain nanofiller-MPTS with filler/resin rasio (50/50) were statistically significant higher than dental composite prototype contain nanofiller-TMPS with same ratio (p<0.05). Otherwise, dental composite prototype with filler/resin ratio (80/20) were no observed statistically significant differences for both nanofiller-TMPS and nanofiller-MPTS (p>0.05). As conclusion, nanofiller modified MPTS are more effective to elevate surface hardness of dental composite prototype than nanofiller-TMPS for 50/50 filler/resin ratio
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.