Abstract
To achieve effective antioxidation of on-site repair coating for C/C brake materials in the full temperature range (500–900 °C), lead glass and bismuth glass were introduced into the borosilicate glass to acquire the protective coatings. Before preparing coating samples, the thermal gravity characteristics of the lead/bismuth–borosilicate glass powders were analyzed by TG/DSC. The results revealed that the temperature at which weight gain begins was 495 °C and 545 °C, respectively. The oxidation behaviors of the lead- and bismuth-modified borosilicate glass coatings were compared at 500 °C, and the antioxidation properties of the former were further examined from 500 to 900 °C. The oxidation results indicated that mixing lead glass with borosilicate glass realized effective oxidation resistance in the full temperature range. With a lead content of 20%, the lead–borosilicate glass coating was able to protect C/C substrates from oxidation. The corresponding weight loss of the lead-glass-coated samples was −1.89% when oxidized at 500 °C for 10 h, while the weight loss was −2.55% when further oxidized at 900 °C for 10 h. However, mixing bismuth glass with borosilicate glass was difficult to achieve the oxidation resistance of the coating at 500 °C due to the significant phase separation.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.