Abstract
Nanocrystalline Cu-Zn ferrites have been synthesized using precursor method. Cu-Zn ferrites were formed at low temperature without any impurities. The particle sizes were observed to decrease from 60 nm to 50 nm with increasing non-magnetic Zn doping. Cu is used to decrease the sintering temperature. The X-ray diffraction (XRD) and IR analysis of Cu-Zn revealed the formation of Single-Phase Spinel structure at very low annealing temperature. The particle sizes observed from XRD is very well in agreement with SEM analysis. Cu-Zn ferrite nanoparticles were observed to be dependent on the particle size. Saturation (Ms) and Remanence (Mr) magnetization of ferrites increases due to the modifications occurred among the A-B, A-A and B-B interactions of Spinel structure. The Coercive force (Hc) decreases with increase of Zn ions concentration.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: International Letters of Chemistry, Physics and Astronomy
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.