Effect on Corrosion Resistance of Ce-Rich-Sealed Ni-P Coatings on Cf/Al Composite Surface

Abstract

In this study, Ni-P coatings and sealing of the coatings by Ce-rich solution on Cf/Al composite surface for enhanced corrosion resistance are investigated. The corrosion resistance of uncoating sample in 3.5 wt.% NaCl solution was investigated and a comparison with Ni-P and Ce-sealed Ni-P coatings is given. Effect of Ce-sealing on Ni-P coating is discussed. The results of electrochemical measurements of corrosion performance of Cf/Al composites show that sealing of Ni-P coatings with Ce-rich solution can improve the corrosion resistance. The Ce-rich-sealed Ni-P coating has higher corrosion resistance than the coating without Ce, and the electroless plated Ni-P coating on composite surface has higher corrosion resistance than the bare sample, as evidenced by EIS and potentiodynamic polarization measurements. The microstructure of the Cf/Al composites and the two kinds of coatings (i.e., Ni-P coating and Ce-sealed Ni-P coating) were examined by scanning electron microscopy, energy dispersive spectroscopy, and transmission electron microscopy. The Ce-sealed Ni-P coatings on Cf/Al composite surface have a total thickness of ~11 μm of which 10 μm is the thickness of the Ni-P coating and ~1 μm is the thickness of the Ce-rich sealing. It shows that the selected area electron diffraction ring pattern of Ce-rich sealing on Ni-P plated composite is consistent with Ce6O11 or CeO2. X-ray photoelectron spectroscopy results show that Ce4+ was the dominant oxidation state for Ce-rich sealing on Ni-P plated composite. The Ce-sealing treatment on Ni-P coating has improved the corrosion resistance over and above the corrosion resistance offered by the Ni-P mono-coating to the bare substrate.