Abstract
In order to satisfy the demand for mullite porous ceramics with complex geometries in the engineering field, the digital light processing (DLP) technology is employed to prepare mullite porous ceramics in this study. However, the poor mechanical properties of the mullite porous ceramics prepared using the DLP technology limits its further application in engineering field. In this work, the microstructure of mullite crystals was regulated by adding the sintering aid ZrSiO4 to enhance the mechanical properties of the mullite ceramics, and the effects of sintering aid ZrSiO4 content and sintering temperature on the internal microstructure evolutions of mullite porous ceramics were investigated. Results showed that the decomposition of ZrSiO4 promoted the generation of the silica-rich liquid phase at high temperatures, which effectively promoted the nucleation and growth of needle-like mullite crystals. When the sintering temperature was 1600 °C and the ZrSiO4 content was 10 wt%, the well-developed elongated crystals formed an interlocking nonwoven structure. The corresponding mullite porous ceramics exhibited a compressive strength of 2.52 MPa and a porosity of 74.51%. The strategy of this study can be a feasible route for preparing lightweight and high-strength mullite porous ceramics via digital light processing.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.