Abstract
Forsterite was found to the next potential candidate for bone implant application due to its superior mechanical properties as compared to the commonly used hydroxyapatite (HA). Various methods including two-step sintering and improvise synthesis method were introduced in hope to further improve the mechanical properties of forsterite. In this work, sintering additives, particularly zinc oxide (ZnO), was introduced into forsterite to provide enhancement on the densification of forsterite at lower sintering temperature. Forsterite powder was synthesized via solid-state reaction method with heat treatment at 1000°C for 2 hours with 10°C/min ramping rate. Addition of ZnO was conducted using milling process with composition of 0.5 wt% and 1.0 wt% ZnO. Green bulk samples were prepared prior to sintering process at 1200°C to 1500°C for 2 hours with 10°C/min ramping rate. Characterization was conducted in terms of phase stability and densification of forsterite with morphology examination to observe the grain surface of all samples. It was revealed that the addition of ZnO showed a more superior densification as compared to the undoped samples at all sintering regime studied with a maximum relative density obtained at 97.7% by 0.5 wt% ZnO doped sample sintered at 1500°C.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: IOP Conference Series: Materials Science and Engineering
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.