Abstract
AbstractAlumina‐based ceramic cores are used to manufacture the internal structures of hollow alloy blades, requiring both high precision and moderate properties. In this work, zirconia is regarded as a promoter to improve the mechanical properties of sintered ceramic. The effect of zirconia content and particle size on the microstructure and mechanical properties of ceramics was evaluated. The results indicate that the flexural strength of sintered ceramics reached the maximum of 14.5 ± 0.5 MPa when 20 wt% micron‐sized (10 μm) zirconia (agglomerate size, consistent with the alumina particle size) was added, and 26.5±2.5 MPa when 15 wt% 0.3 μm zirconia was added. Zirconia with submicron‐sized (0.3 μm) particles effectively filled the pores between alumina particles, thus leading to the maximum flexural strength with a relatively low content. The corresponding sintered ceramics had a bulk density of 2.0 g/cm3 and open porosity of 59.6%.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.