Abstract
The effects of a third element, i.e., Zn in the range of 0.5–2.5 wt.%, on structure and properties of the binary Sn–Ag eutectic lead-free solder alloy were investigated. To identify the structure of the resulting alloys, X-ray diffraction analysis has been carried out. Resistivity, contact angles, Vickers microhardness and Young’s modulus have been measured. The results showed that all Zn contents were restricted in formation of Ag-Zn compound indicated by X-ray diffraction peaks, which increased continuously in the number and intensity as Zn content increased. Adding Zn up to 1.5 wt.% improved the wetting and mechanical properties. Above that, wetting angle increased due to the increase in AgZn compound, which may accumulated at the interface between solders and copper- substrate resulting a decrease in the adhesive strength. The alloy of composition Sn-3.5Ag-1.5Zn has the most improved properties between the others.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: Journal of Materials Science: Materials in Electronics
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.