Abstract
In this study, La0.8-xYxSr0.2MnO3 (LYSMO) polycrystalline ceramics were prepared by means of sol-gel technique using methanol as solvent. X-ray diffraction (XRD) showed all samples to possess standard perovskite structure. Scanning electron microscopy (SEM) revealed samples with high compactness and grain size from 27.80 to 29.73 μm. Resistivity–temperature tests indicated sharp metal-insulator transition behavior of all samples accompanied by rapid transformation from ferromagnetism to paramagnetism (FM-PM). As Y3+ doping amounts rose, radius of A-site ions decreased, metal-insulator transition temperature (Tp) of polycrystalline samples shifted to lower temperatures, and resistivity increased. Temperature coefficient of resistance (TCR) and magnetoresistance (MR) were affected by introduction of Y3+. At x = 0.06, peak TCR and peak MR reached 4.85% K−1 and 52.34%, respectively. Using double exchange (DE) interaction mechanism, electric transport performances of as-prepared ceramics were explained. These findings look promising for future applications of LYSMO materials in magnetic devices and infrared detectors.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.