Effect of wood sawdust content on rheological and structural changes, and thermo‐mechanical properties of PVC/sawdust composites

Abstract

AbstractThe use of untreated sawdust as a filler in poly(vinyl chloride) (PVC) was examined—the effects of sawdust content on structural and thermal changes, and rheological and mechanical properties being of main interest. The results revealed that the torque and die entrance pressure drop values during mixing were independent of sawdust particles up to 23.1 wt%. The extrudate swell monotonically decreased up to 33.3 wt% sawdust content. Smooth wood‐like texture with controllable size of the extrudate could be obtained at a sawdust content greater than 33.3 wt%. Tensile, impact, flexural and hardness properties of the PVC/sawdust composites considerably decreased with up to 16.7 wt% sawdust content before leveling off for higher sawdust loadings. The composites having sawdust higher than 16.7 wt% showed a benefit of cost savings. The decreases in the mechanical properties of PVC with sawdust are explained in association with the presence of moisture, interfacial defects between fibre and polymer, and fibre dispersions in the PVC matrix. Thermal degradations of PVC in PVC/sawdust composites were evidenced by a decrease in decomposition temperature and an increase in polyene sequences, which were caused by Cl cleavage due to strong hydrogen bonds of fibre–PVC molecules. The maximum of tanδ transition and the glass transition temperature were found to improve with sawdust content as a result of re‐formation of hydrogen bonds between the macromolecules of the fibre and the polymer. The overall results in this work suggest that the properties of PVC/sawdust composites were strongly influenced by sawdust content up to 16.7 wt%. Beyond this value the effect of sawdust content on the properties was comparatively small. Copyright © 2003 Society of Chemical Industry