Effect of weld metal composition and welding conditions on δ -ferrite and CVN toughness of austenitic-ferritic weld metal

Abstract

In the present investigation, the effect of base plate and filler wire composition as well as of welding conditions on δ-ferrite contents and toughness of austenitic-ferritic stainless steel weld metal has been established. According to previous work, the δ-ferrite contents are not only depending on chemical composition but also on cooling conditions of the weld metal. The application of δ-γ-CCT diagrams is recommended. Increasing δ-ferrite contents lower the CVN toughness of the weld metal, which should be taken into consideration before recommending filler materials and welding conditions. In der vorliegenden Arbeit wurde der Einfluß der Zusammensetzung von Grundblechwerkstoff und Schweißzusatz wie auch der Einfluß der Schweißbedingungen auf die Ausbildung von δ-Ferrit und auf die Zähigkeit von Schweißgut aus austenitisch-ferritischem nichtrostendem Stahl untersucht. In Übereinstimmung mit früheren Arbeiten wurde festgestellt, daß die δ-Ferritgehalte nicht nur von der chemischen Zusammensetzung, sondern auch von den Abkühlbedingungen des Schweißgutes abhängig sind. Hierzu wird die Anwendung von ZTU-Schaubildern mit kontinuierlicher Abkühlung für den Umwandlungsbereich δ/γ empfohlen. Es zeigte sich, daß mit Zunahme der δ-Ferritgehalte die an ISO-V-Proben ermittelte Kerbschlagarbeit herabgesetzt wird; dies sollte bei der Auswahl von Schweißzusätzen und -bedingungen berücksichtigt werden.