Abstract
Abstract This study deals with the microstructure and mechanical properties of WC–(W, Ti, Ta) C–9 vol.% Co cemented carbides fabricated by conventional sintering. The conventional WC particles of 4 μm size and ultrafine particles of 0.2 μm were introduced in the system with varying ratio. The ratios of conventional WC particles to ultrafine WC particles were 2:1, 1:1, and 1:2. The microstructures of sintered WC–(W, Ti, Ta) C–9 vol.% Co cemented carbides were sensitively dependent on the ratio of conventional WC particles to ultrafine WC particles. The rim phase increased with the increase in the amount of ultrafine particles. Hardness of WC–(W, Ti, Ta) C–9 vol.% Co cemented carbide increased with increase in the amount of rim phase and decrease in the average grain size of WC particles. The bending strength showed the similar trend of the hardness. The fracture morphologies are reported. The fracture behavior changed from mixed mode to transgranular fracture mode, when the ratio of conventional WC particles to ultrafine WC particles was changed from 2:1 to 1:2.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: International Journal of Refractory Metals and Hard Materials
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.