Abstract
(Ge2Sb2Te5)90Ag10 (GST-Ag) bulk alloy was prepared using melt quenching technique. GST-Ag thin film was deposited on glass substrate using thermal evaporation method. The prepared thin films were exposed to visible light (intensity of 105 Lux for 2, 8, 20 and 30 hours) using 25W LED lamp. Transmission spectra were taken using UV-vis-NIR spectrophotometer in the wavelength range 800-3200 nm. Optical band gap of as-deposited and light exposed thin films was determined using Tauc’s plot. Optical band gap was found to be decreasing on light exposure upto 8 hours and after that no significant change was observed.(Ge2Sb2Te5)90Ag10 (GST-Ag) bulk alloy was prepared using melt quenching technique. GST-Ag thin film was deposited on glass substrate using thermal evaporation method. The prepared thin films were exposed to visible light (intensity of 105 Lux for 2, 8, 20 and 30 hours) using 25W LED lamp. Transmission spectra were taken using UV-vis-NIR spectrophotometer in the wavelength range 800-3200 nm. Optical band gap of as-deposited and light exposed thin films was determined using Tauc’s plot. Optical band gap was found to be decreasing on light exposure upto 8 hours and after that no significant change was observed.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.