Abstract
Bi3.25La0.75Ti3O12 (BLT) and V-doped BLT (BLTV) thin films were prepared on Pt/Ti/SiO2/Si substrates by a pulsed laser deposition method. The effects of V doping on ferroelectric and electrical properties were investigated by polarization-electric field hysteresis loops and leakage current-voltage measurements. BLTV single phases were confirmed by X-ray diffraction. Remnant polarization was increased and the leakage current density was decreased by V doping. The leakage current density of BLT thin films suddenly increased at 100 kV/cm while that of BLTV thin films increased at the higher electric field of 160 kV/cm. The power law relationship J α En of current density vs. applied electric field is estimated to be J αE2.0 for BLT and J αE1.0 for BLTV thin films. The leakage current of the BLT/Pt junction can be explained by space-charge-limited current. However, that of the BLTV/Pt junction was characterized by the Schottky emission behavior.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.