Abstract
The authors studied the effect of vanadium addition on the microstructure and properties of Al0.5CoCrCuFeNi high-entropy alloy. The microstructure of Al0.5CoCrCuFeNiV x (x=0 to 2.0 in molar ratio) alloys was investigated by scanning electron microscopy, energy dispersive spectrometry, and X-ray diffraction. With little vanadium addition, the alloys are composed of a simple fcc solid-solution structure. As the vanadium content reaches 0.4, a BCC structure appears with spinodal decomposition and envelops the FCC dendrites. From x=0.4 to 1.0, the volume fraction of bcc structure phase increases with the vanadium content increase. When x=1.0, fcc dendrites become completely replaced by bcc dendrites. Needle-like σ-phase forms in bcc spinodal structure and increases from x=0.6 to 1.0 but disappears from x=1.2 to 2.0. The hardness and wear resistance of the alloys were measured and explained with the evolution of the microstructure. The hardness values of the alloys increase when the vanadium content increases from 0.4 to 1.0 and peak (640 HV) at a vanadium content of 1.0. The wear resistance increases by around 20 pct as the content of vanadium increases from x=0.6 to 1.2 and levels off beyond x=1.2. The optimal vanadium addition is between x=1.0 and 1.2. Compared with the previous investigation of Al0.5CoCrCuFeNi alloy, the vanadium addition to the alloy promotes the alloy properties.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.