Abstract
The effect of V/III ratio on the growth and properties of AlGaN layers grown on (112¯2) AlN templates grown on (101¯0) sapphire by metalorganic vapour phase epitaxy was studied. The surface morphology of the (112¯2) AlGaN layers and the (112¯2) AlN templates showed an undulation along [11¯00]AlGaN,AlN. The Al-content and thickness of the layers increased with decreasing V/III ratio due to a reduction in the parasitic reactions of the precursors. The Al-content of the (112¯2) layers was found to be in the range of 29.5−47.9%, which is lower than the composition of the simultaneously grown (0001) reference layers (30.4−58.0%). This was attributed to a higher density of cation (nitrogen) dangling bonds on the (112¯2) surface. Low temperature photoluminescence measurements of the (112¯2) layers showed an emission wavelength that shifts gradually from 273nm to 306nm with increasing V/III ratio. A decreased PL intensity of the layers with decreasing V/III ratio was attributed to an increase in cation vacancies. The Stokes-shift of the (112¯2) layers was estimated to be about 60−194meV, and this shift increases with increasing Al-content (decreasing V/III ratio) correlated to an increased exciton localization.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.