Abstract
AbstractEffects of ultrasonic nanocrystal surface modification (UNSM) on the very high cycle fatigue response of AISI 310 stainless steel have been investigated. The higher impact force used in UNSM treatment showed a higher fatigue life improvement. The fatigue life improvement was higher in crack initiation from the surface of specimens. The subsurface crack initiation depth in the alloy increased with increase in the fatigue failure cycles. It was concluded that UNSM treatment can increase the life of the alloy significantly up to very high cycle fatigue.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: Fatigue & Fracture of Engineering Materials & Structures
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.