Abstract
Martensitic high-carbon high-strength SUJ2 bearing steel has been widely used as a main alloy for rolling contact applications, and also in components under bending and tension-compression. In order to enhance the material’s strength, refining the prior austenite grain size through repeated-heating was investigated in our previous work. In this work, we observed the microstructure of twice quenched N-rich SUJ2 steel and performed their rotating bending fatigue tests. It was found that most of cracks on the fracture surface originated from Al2O3 inclusions.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.