Abstract
The effects of tritium on the corrosion behavior of chromium were investigated in the present study, since it was suggested in the previous studies that the elution of chromium, which is one of the main constituent elements of passive layer of SUS 304 stainless steel, during passivation through further oxidation induced by oxidative radiolysis products would be the key reaction for the enhancement of the corrosion of SUS304 stainless steel induced by tritium. As the experimental results of the dependence of both dissolved oxygen and tritium concentration on the anodic behavior of chromium, it was found that the self-passivation of chromium induced by dissolved oxygen was inhibited in the tritiated solution, as found in the previous studies for SUS304 stainless steel. Therefore, it was considered that the elution of chromium by highly oxidative radiolysis products would induce a passivation inhibitory effect onto SUS304 stainless steel in a tritiated solution, resulting in an enhancement of the corrosion.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.