Abstract
Nano-structured TiAlCrYN coatings, grown by unbalanced magnetron sputtering on various steel substrates, exhibited friction coefficients 0.6–0.8 and wear coefficients 10−16–10−15 m3 N−1 m−1 in dry sliding wear tests. This article reports comprehensive worn surface analyses using SEM, TEM, EDX, EELS and Raman spectroscopy. A ~80 nm thick tribofilm formed on the TiAlCrYN worn surface was found to have dense amorphous structure and homogeneous oxide composition of Cr0.39Al0.19Ti0.20Y0.01O0.21. Viscous flow of the amorphous tribofilm was dominant in causing the high friction coefficient observed. The coatings showed combined wear mechanisms of tribo-oxidation and nano-scale delamination.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.