Abstract
A nanocrystalline surface layer of low carbon steel induced by fast multiple rotation rolling (FMRR) was determined by optical microscopy and transmission electron microscopy. The results show that the grain size decreases gradually with the increase of treatment duration. Equiaxed nanocrystalline with the average grain size about 20nm is obtained in the top surface layer after FMRR treatment for 30min. With the increase of treatment duration (60min), the average grain size further reduces to about 9nm. At the same time, the microhardness of surface layer for treated sample is improved correspondingly owing to grain refinement and work-hardening. Compared with original sample, the microhardness of FMRR treated sample is increased by more than 200%. After annealing treatment, the investigation of thermal stability of nanocrystalline layer indicates that the grains begin to grow obviously at annealing for 400°C, and abnormal grain growth also occurs in individual grains. Due to grain growth and stress relaxation during annealing, the microhardness slightly decreases at 400°C. In spite of this, the majority of grains are still nanocrystalline, ranging from about 30 to 60nm. It demonstrates that the nanocrystalline layer has high thermal stability.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.