Abstract
A study has been made of the combined effects of composition and travel speed on solidification cracking in the autogenous tungsten inert gas arc welding of low-alloy steel sheet. Data were obtained using the Huxley cracking test for steels to specifications En 24, SAE 4130, and ASTM A 387 B with a range of carbon, sulphur, phosphorus, and oxygen contents. A strong and complex effect of travel speed on cracking susceptibility was revealed, the form of the relationship being determined by the composition of the steel. At high carbon, high sulphur, high phosphorus, and/or low oxygen contents cracking was severe at low speeds but fell progressively to low values at high speeds. At low carbon, low sulphur, low phosphorus, and/or high oxygen contents cracking was low at both low and high speeds with a maximum at an intermediate speed. It is demonstrated that increased travel speed decreases the transverse crack-promoting forces at the rear of the pool but increases the length of the crack-susceptible zone. These effects are used to account for the reported interaction of composition and speed on cracking behaviour. Consideration is given to the significance of the results for welding production and welding test procedure with these steels.
Published Version
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.