Abstract
Tensile and low cyclic fatigue tests were used to assess the influence of micro-additions of Ti/V/Zr on the performance of Al–7Si–1Cu–0.5Mg (wt.%) alloys in the as-cast and T6 heat-treated conditions and their improvement was compared to the base alloy. The microstructure of the as-cast Al–7Si–1Cu–0.5Mg (wt.%) base and modified alloys consisted of α-Al, eutectic Si, and Cu, the Mg- and Fe-based phases Al2.1Cu, Al8.5Si2.4Cu, Al7.2Si8.3Cu2Mg6.9 and Al14Si7.1FeMg3.3. In addition, the micro-sized Ti/V/Zr-rich phases Al6.8Si1.4Ti, Al21.4Si4.1Ti3.5VZr3.9, Al6.7Si1.2TiZr1.8, Al2.8Si3.8V1.6Zr and Al5.1Si35.4Ti1.6Zr5.7Fe were identified in the modified alloys. It was also noticed that increasing the content of Ti–V–Zr changed the morphology of Ti/V/Zr-rich phase. The tensile test results showed that the T6 heat-treated alloy modified with the addition of a higher content of Ti–V–Zr achieved the highest tensile strength of 343MPa over the base alloy and alloys modified with additions of Ti, Ti–Zr and lower contents of Ti–V–Zr. The plastic strain energy density coefficient of the alloy modified with the addition of a higher content of Ti–V–Zr in the T6 temper condition was higher than the other studied alloys and reached 162MJm−3. The fatigue life of the same alloy was considerably longer than that of the other studied alloys, including the base alloy. The fractography revealed that all the studied alloys showed similar fracture behavior. The tensile cracks propagated through the eutectic Si and primary phases, exhibiting intergranular fracture along with some cleavage-like features of the plate-shaped Zr–Ti–V-rich intermetallics with the presence of fatigue striations on the latter, indicating their ductile nature. It is believed that the morphological changes of intermetallic precipitates containing Zr, Ti and V enhance the fatigue life of the alloy modified with additions of larger amounts of Ti–V–Zr in the T6 condition.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.