Abstract
AbstractBorosilicate glasses doped with PbSe quantum dots (QDs) were prepared by a conventional melt‐quenching process followed by heat treatment, which exhibit good thermal, chemical, and mechanical stabilities, and are amenable to fiber‐drawing. A broad near infrared (NIR) photoluminescence (PL) emission (1070‐1330 nm) band with large full‐width at half‐maximum (FWHM) values (189‐266 nm) and notable Stokes shift (100‐210 nm) was observed, which depended on the B2O3 concentration. The PL lifetime was about 1.42‐2.44 μs, and it showed a clear decrease with increasing the QDs size. The planar [BO3] triangle units forming the two‐dimensional (2D) glass network structure clearly increased with increasing B2O3 concentration, which could accelerate the movement of Pb2+ and Se2− ions and facilitate the growth of PbSe QDs. The tunable broadband NIR PL emission of the PbSe QD‐doped borosilicate glass may find potential application in ultra‐wideband fiber amplifiers.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.