Abstract
Morphologies, microstructure and composition distribution of the magnesium anodic materials were studied by metallographic microscopy, x-ray diffraction (XRD), scanning electron microscope (SEM) and energy dispersive spectroscopy (EDS). The corrosion behavior and electrochemical properties of Mg alloy were also investigated by constant current method, potential polarization, collecting gas through drainage. The results show that tin restrained β-Mg17Al12 phase precipitation along the grain boundary. With the content of tin increasing, granular Mg2Sn phase was improved. After uniform heat treatment, most of β-Mg17Al12 phase was dissolved, but most of Mg2Sn was not dissolved. Tin could improve self-corrosion potential and release hydrogen rate. Magnesium alloy anode with 1% tin content had high discharge potential and current efficiency. With the current density increasing, the release hydrogen rate augmented. The current efficiency reached 82 % at 20mA/cm2. The main composition of the corrosion products were MgO and Al2O3 which were easily peeled off. As a result, more negative and stable work potential was produced and the reaction was accelerated continuously.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.