Abstract
Purpose The purpose of this paper is to investigate the effect Ti on stress corrosion cracking (SCC) and flow accelerated stress corrosion cracking (FA-SCC) behavior and mechanisms of Monel K500 alloy. Design/methodology/approach Monel K500 alloy with different Ti contents was designed. A metallurgical microscope (XJP-3C) and scanning electron microscopy (EV0 MA15 Zeiss) with an energy dispersive spectroscopy were used to analyze the microstructure of the Monel K500 alloy. In situ electrochemical tests were carried out in static and flowing seawater to study FA-SCC behavior. Findings The number of TiCN particles in the alloy increased as the increase of Ti content. The static corrosion and SCC of Monel K500 alloy are reduced as the content of Ti increases. Generally, the SCC of alloys was caused by the synergistic effect of the anodic dissolution at exposed metal matrix and the pit corrosion of metal matrix adjacent to TiCN particles, which was further accelerated by flowing. Originality/value The corrosion behavior and mechanism of Monel K500 alloy with different Ti contents in a complex flowing seawater environment are still unclear, which remain systematic study to insure the safe service of the alloy.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.