Abstract
AB 5-type intermetallic compounds were prepared by arc-melting in an argon atmosphere. The composition of a stoichiometric compound ( LMNi 3.6 Al 0.4 Co 0.7 Mn 0.3) M y ( LM= La -rich mischmetal , M=Ti, Zr; y=0.0, 0.02, 0.05, 0.1, 0.2, 0.3 ) with a hexagonal CaCu 5 structure was varied by stoichiometric and nonstoichiometric addition of Ti or Zr. The alloy surface was analyzed by energy-dispersive spectroscopy and scanning electron microscopy and the crystal structure was characterized by X-ray diffraction. To determine hydrogen storage capacity, the pressure composition isotherms (PCT curves) were utilized. Metal hydride electrode was characterized by galvanostatic cycling test. It was found that the addition of Ti ( y=0.05) or Zr ( y=0.02) improves the activation, discharge capacity and cycle life property. But, the alloy with Ti addition ( y⩾0.2), containing a Zr addition ( y⩾0.2), is found to have bad discharge capacity and cycle life. The kinetic properties are additionally increased by the formation of a Ti- or Zr-rich second phase. The improvement in discharge capacity caused by increasing the Ti or Zr content (0.1⩾ y) in the alloy is attributed to active sites for the electrochemical reaction. Also, they seem to be strongly related with the shapes and amounts of the second phases.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.