Abstract
Through-thickness friction stir processing was successfully carried out for microstructure modification and elimination of fusion defects of the gas metal arc welds by applying the process on as-welded joints. Variation in rotational speed from 750 to 1050 rpm and traveling speed from 50 to 200 mm/min resulted in minor changes (approximately 1 µm) in the grain size of nugget zone, while this variation in elongation result was up to 40%. The hardness profile, the width of softening zone, minimum hardness and fracture location also changed for different processing conditions. Furthermore, the defects were vanished efficiently across the welds profile by this method. The results also verified the geometric dynamic recrystallization phenomena as a dominant mechanism of microstructural modification.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.