Abstract

RHA–Al 2O 3 composite oxide supports were prepared by impregnation of rice husk ash with an aluminum sulfate solution, and were then used to prepare Ni/RHA–Al 2O 3 catalysts by the ion exchange method. The supports and catalyst precursors were characterized by X-ray diffraction (XRD) and transmission electron microscopy (TEM). The thermal decomposition of catalyst precursors was examined by a thermogravimetric analyzer (TGA). In addition, the effect of calcination temperature on the catalyst reducibility was investigated by the temperature-programmed reduction (TPR) technique. Results show that the decomposition temperature of layered nickel compound to nickel oxide started above 773 K. Reduction in NiO from the thermal decomposition of the layered nickel compound was found to be particularly difficult. The reduction temperature increased with the increase in calcination temperature. The catalytic activities of nickel catalysts were tested by CO 2 hydrogenation with H 2/CO 2 ratios of 4/1 at 773 K. The effects of calcination temperature, calcination time, reduction temperature, reduction time and alumina content on the activity of catalysts were examined extensively. An optimal condition for calcination and reduction of catalysts has been determined from activity considerations in the hydrogenation of CO 2.

Full Text
Published version (Free)

Talk to us

Join us for a 30 min session where you can share your feedback and ask us any queries you have

Schedule a call