Effect of thermal annealing on grain boundary chemistry of polycrystalline TiBa2Ca2Cu3Oy films

Abstract

Recent studies have shown that spray-pyrolyzed films of the Tl-1223 compound (TlxBa2Ca2Cu3Oy, with 0.7 < × < 0.95) on polycrystalline yttrium stabilized zirconia substrates can be prepared which have critical current density Jc near 105 A/cm2 at 77 K, in zero field. The films are polycrystalline, have excellent c-axis alignment, and show little evidence of weak-link behavior. Transmission electron microscopy (TEM) studies have shown that most grain boundaries have small misorientation angles. It has been found that the films have a nigh degree of local texture indicative of colonies of similarly oriented grains. It is believed that inter-colony conduction is enhanced by a percolative network of small angle boundaries at colony interfaces. It has also been found that Jc is increased by a factor of 4 - 5 after the films were annealed at 600 °C in oxygen. This study is thus carried out to determine the effect on grain boundary chemistry of the heat treatment.