Abstract
The effects of thermal aging at 85~145 °C in air on the tensile and flexural mechanical properties of 20% glass fiber (GF)-reinforced commercial grade polybutylene terephthalate (PBT) composites were studied. The results showed that as the aging temperature increased, the tensile and flexural strength of the GF/PBT composites significantly decreased. However, the elastic modulus of the composites was almost independent of aging. As the aging temperature increased, the separation between GF and the PBT matrix became more pronounced, and the fibers exposed on the surface of the matrix became clearer and smoother, indicating a decrease in interfacial adhesion between the PBT matrix and GF. The reason for this decrease in strength and brittle fracture of composites is the interface damage between the GF and PBT matrix caused by the difference in their thermal expansion coefficients during thermal aging.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.