Abstract

Polydimethylsiloxane (PDMS) films were treated with either oxygen (O2), nitrogen (N2) or argon (Ar) plasma between 40W and 120W for 5–15min and their surface properties studied by contact angle measurements, infrared spectroscopy (FTIR), scanning electron microscopy (SEM) and atomic force microscopy (AFM). Lower contact angles and increases in surface roughness, assessed by SEM and AFM, were observed for all used gases when plasma power and time increased, with argon treatment being the one that showed the most significant change in roughness.PDMS/collagen type I composites obtained after treating PDMS with oxygen at 80W for 13min or nitrogen and argon at 80W for 14min showed a peel strength of 0.1N/mm (oxygen plasma), 0.08 N/mm (nitrogen plasma) and 0.09 N/mm (argon plasma). In all cases, peel strength was higher than that measured for the untreated bilayer composite. An increase in adhesion strength, after oxygen and nitrogen plasma, was mostly attributed to chemical interaction between functional groups introduced on the PDMS surface and the functional groups on collagen as detected by FTIR. In contrast, the high peel strength observed on PDMS treated with argon plasma was attributed to its increased roughness which in turn increased mechanical interlocking. The properties of these composites render them suitable for adhesive free skin substitutes.

Full Text
Paper version not known

Talk to us

Join us for a 30 min session where you can share your feedback and ask us any queries you have

Schedule a call

Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.