Al2O3 coatings with different thicknesses (160, 320, 480 and 640μm) were deposited on stainless steel substrate by plasma spraying. The variation in microstructural characteristics and properties of coatings with various thicknesses was investigated. Powders morphology and the microstructure of as-sprayed coatings were characterized by scanning electron microscopy and optical microscopy. The microhardness was measured using a Vickers' indentor. The corrosion behaviour of plasma-sprayed Al2O3 coatings in 1N H2SO4 solution at a temperature of 25°C was evaluated by electrochemistry method. Experimental results indicated that surface roughness showed no obvious dependence on the coating thickness. However, the porosity of Al2O3 coating was increased with increased thickness. The enhanced coating thickness also resulted in decreasing microhardness and reduced corrosion resistance. In this study, the Al2O3 coating with thickness of 160μm possesses the lowest porosity, the highest hardness and superior corrosion resistance.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.