Effect of the preparation condition on the properties of titania-silica derived from tetraisopropyl titanate(IV) and tetraethyl orthosilicate

Abstract

Titania-silica mixed oxide was prepared by hydrolyzing tetraethyl orthosilicate and tetraisopropyl titanate(IV) with a mixture of ethanol and 0.01 N aqueous acetic acid. Surface Ti content, BET surface area, and the number of acid sites increased with an increase in 0.01 N aqueous acetic acid. Thus hydrolysis of both alkoxides occurred simultaneously with a large amount of the acetic acid solution, and there was extensive interaction between TiO2 and SiO2 phases. With small amount of 0.01 N aqueous acetic acid, however, titanium hydroxide was first formed and, then, it was covered with the silica phase produced in a later stage of the hydrolysis. Increase in the acetic acid solution also led to the formation of a large amount of tetrahedral Ti species, which were active for the epoxidation of oct-1-ene usingt-butyl hydroperoxide as an oxidant.