Abstract
The effect of La3+ ions substitution on the magnetic properties of the composition Li0.5−0.5xZnyLaxFe2.5−0.5x−yO4 (0.02≤x≤0.1; y=0.6) was studied. The structure of the samples was investigated using X-ray, SEM and IR. Both of zero field cooled (ZFC) and field cooled (FC) modes magnetization were studied at low temperature range (2K≤T≤400K). Magnetization applied field-dependence (M–H) curves were measured at low temperature (5K). The experimental data revealed that the samples exhibited a phase transition from ferrimagnetic state at low temperature to paramagnetic state at high temperature (400K). The obtained Curie temperature was shifted to lower value with La3+-content. The M–H carves showed that the samples are soft ferromagnetic and it can be an excellent candidate for industrial applications.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.