Abstract
PurposeThis study aims to investigate the effect of countersunk rivet head dimensions on the fatigue performance of the riveted specimens of 2024-T3 alloy.Design/methodology/approachThe relationship between rivet head dimensions and fatigue behavior was investigated by finite element method and fatigue test. The fatigue fracture of the specimens was analyzed by scanning electron microscopy.FindingsA change of the rivet head dimensions will cause a change in the stress concentration and residual normal stress, the stress concentration near the rivet hole causes the fatigue crack source to be located on the straight section of the countersunk rivet hole and the residual normal stress can effectively restrain the initiation and expansion of fatigue cracks. The fatigue cycle will cause the rivet holes to produce different degrees of surface wear.Originality/valueThe fatigue life of the specimens with the height of the rivet head of 2.28 mm and 2.00 mm are similar, but the specimens with the height of the rivet head of 1.72 mm were far higher than the other specimens.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.