Abstract
This paper examines the effects of the mixture ratio of fly ash/slag, the type of alkaline activators and curing conditions on the workability, compressive strength and microstructure of cementless alkali-activated mortar. The investigation showed that the mixture ratio of fly ash/slag and the type of alkaline activator have significant influence on the workability and strength, whereas the curing temperature has relatively poor effect. An alkali-activated mortar using a binder composed of 50% of fly ash and 50% of granulated blast furnace slag and alkaline activator made of 9M NaOH and sodium silicate in proportion of 1:1 is seen to be able to develop a compressive strength of 65 MPa at age of 28 days even when cured at ambient temperature of 20°C.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.