Abstract
The comparison of the different aluminum sources including: α-Al 2O 3, θ-Al 2O 3, γ-Al 2O 3 and boehmite to form the yttrium aluminum garnet (YAG) powder via the solid state reaction method are studied in this article. According to the experimental results, we can conclude that boehmite (AlOOH) is the best aluminum source for the formation of YAG powder. The intermediated phases, such as YAM(Y 2Al 4O 7) and YAP(YAlO 3), were presented at 1200 °C and the impure phase α-Al 2O 3 was formed at 1500 °C for 1 h. A pure YAG phase was successfully formed from the reacting product of yttrium oxide and boehmite after calcining at 1500 °C for 5 h.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.