Abstract
The results obtained by partially substituting Ge for B and Si in the FINEMET alloy for the purpose of improving its magnetic properties at high temperatures are presented in this work. Nanocrystalline ribbons were obtained from controlled crystallization of amorphous material made employing the melt spinning technique. The studied compositions were: Fe 73.5Si 13.5Ge 2Nb 3B 7Cu 1 and Fe 73.5Si 13.5Ge 4Nb 3B 5Cu 1. The structural evolution of these alloys was studied using X-ray diffraction (XRD) and differential scanning calorimetry (DSC) and these results were correlated with their magnetic properties at different annealing temperatures. The coercivity obtained for both alloys was below 1 A/m at anneling temperatures between 773 and 823 K. The amorphous saturation magnetization was satisfactory, almost 137 emu/g, comparable with that obtained for FINEMET alloys. The nanocrystallization and the Curie temperatures are dependent on Ge concentration.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.