Abstract

AbstractEpoxy functional siloxane (DMS‐E09) was blended with epoxy resin (DGEBA) and thermoplastic polyetherimide (PEI). The results of morphology monitoring indicated that the reaction induced phase separation for all blends followed the spinodal phase separation mechanism. The microstructure changed from co‐continuous of 25 wt% epoxy/PEI system to phase‐inversion structure of 30 wt% epoxy/PEI system regardless of the content of the tertiary component DMS‐E09. By comparing the onset time of phase separation between the two designated systems, the sequential occurrence of primary macrophase separation in co‐continuous phase and secondary microphase separation in PEI‐rich phase for 25 wt% epoxy/PEI system was identified. Studies of the thermomechanical properties of the DGEBA/PEI/DMS‐E09 blends found that storage modulus increased with the addition of PEI but decreased with DMS‐E09 monotonically. The value of Tg decreased with the addition of the tertiary DMS‐E09 but was offset partially by the presence of PEI.

Talk to us

Join us for a 30 min session where you can share your feedback and ask us any queries you have

Schedule a call

Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.