Abstract
The wear behavior of a FeCoNiCrMn (counterbody)–Ti30Zr25Hf15Nb20Ta10 (finger) friction pair in the temperature range of 77–873 K has been determined. It has been found out that the finger wear significantly decreases with an temperature increase compared with the counterbody due to the spur increase in the hardness of the friction surface structures of up to 18.0 GPa due to the formation of a high-temperature oxide. It has been revealed that the depth of secondary structures increases with temperature, while at 523 K and higher, it reaches 40 μm.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.